White Rubber Coated Fiberglass "Tacky Cloth" Tadpole Gaskets
High Temperature & Heat Resistant
High Temperature & Heat Resistant
High-Temperature Tacky Cloth
Tadpole Gaskets
Tadpole Gaskets
550°F / 287°C Continuous
This high temperature and heat resistant tadpole tape is made from Tuff-Flex™ 550 Fabric tacky cloth.
This is a widely used tadpole tape that provides a resilient and non-absorbent gasket material for service against steam, air, water and gases.
Especially useful where a rough or uneven surface or flange exists. The fabric is a fiberglass base with a special white rubber formulation. The fabric is tacky, and has a plastic film surface covering that is removed before installation. The fabric will stick to itself once the film is removed.
Wire Inserted Version: The fill (widthwise) yarn for this version of the fabric has a twisted brass wired formed with it, providing additional strength and electrical conductivity/shielding.
550°F / 287°C continuous rating, excellent sealing properties as a gasket material
This high temperature and heat resistant tadpole tape is made from Tuff-Flex™ 550 Fabric tacky cloth.
This is a widely used tadpole tape that provides a resilient and non-absorbent gasket material for service against steam, air, water and gases.
Especially useful where a rough or uneven surface or flange exists. The fabric is a fiberglass base with a special white rubber formulation. The fabric is tacky, and has a plastic film surface covering that is removed before installation. The fabric will stick to itself once the film is removed.
Wire Inserted Version: The fill (widthwise) yarn for this version of the fabric has a twisted brass wired formed with it, providing additional strength and electrical conductivity/shielding.
550°F / 287°C continuous rating, excellent sealing properties as a gasket material
Curing: It is recommended that this material be cured in situ. This material must be heated to a minimum of 300°F within 60 minutes, then it must sit at 300°F or higher for 90 minutes for the rubber to fully cure.
Do not overtorque the material during this curing time or the rubber will be squeezed off of the base material.
If the material is not fully cured, the rubber will drip from the material causing voids. After curing the material can be exposed to a lower operational temperature.
Do not overtorque the material during this curing time or the rubber will be squeezed off of the base material.
If the material is not fully cured, the rubber will drip from the material causing voids. After curing the material can be exposed to a lower operational temperature.